Products

Eaton Alloys PTE LTD. was established in 2011 (as Eaton Alloys Limited) and has grown consistently over this time to become a specialized supplier for specialty metals widely used in oil a

Online Documents

Data Sheets & Technical Documents

Download articles

Products

Online Documents

Data Sheets & Technical Documents

Download articles





Singapore

Add.: 139 Bedok North Avenue 3, #10-188, Singapore 460139
Tel: 0065 9664 4411
Email:tonytay@eatonalloys.com

Web:www.eatonalloys.com

China

Add.: 489# Guanghua Dong 3rd Road, Chengdu, China, 610091
Tel: 0086 28 81703462
Email: sales@eatonalloys.com
Web: www.eatonalloys.com


Alloy 230

Alloy 230

Alloy 230 is a nickel-chromium-tungsten-molybdenum alloy that combines excellent high temperature strength, outstanding resistance to nitriding environments and excellent long term thermal stability. Alloy 230 is easily fabricated and has very good forming and welding characteristics. Due to Alloy 230 combined properties it is very well suited to a wide variety of component applications in the aerospace and power industries. Alloy 230 is used for combustion cans, transition ducts, flame holders, thermocouple sheaths and other important gas turbine components. Haynes alloy 230 is solution treated at 2150 to 2275°F followed by rapid cooling, and is supplied in this condition (as per AMS 5891 and AMS 5878). Alloy 230 can be both hot worked and cold worked and all parts should be annealed and rapidly cooled in order to restore the best balance of properties.


Nominal Composition %

Ni 57.0
Cr 22.0
W 14.0
Mo 2.0
Fe 3.0 max
Co 5.0 max
Mn 0.5
Si 0.4
Ni 0.5 max
Al 0.3
Ti 0.1 max
C 0.1
La 0.02
B 0.015 max

Mechanical Properties

Alloy 230 extruded bar solution annealed
Tensile Strength 110 ksi
0.2% Yield Strength  45 ksi
Elongation  35%
Hardness 241 HB max

Specifications
UNS N06230
AMS5891
DIN 17744
ASTM B572