Products

Eaton Alloys PTE LTD. was established in 2011 (as Eaton Alloys Limited) and has grown consistently over this time to become a specialized supplier for specialty metals widely used in oil a

Online Documents

Data Sheets & Technical Documents

Download articles

Products

Online Documents

Data Sheets & Technical Documents

Download articles





Singapore

Add.: 139 Bedok North Avenue 3, #10-188, Singapore 460139
Tel: 0065 9664 4411
Email:tonytay@eatonalloys.com

Web:www.eatonalloys.com

China

Add.: 489# Guanghua Dong 3rd Road, Chengdu, China, 610091
Tel: 0086 28 81703462
Email: sales@eatonalloys.com
Web: www.eatonalloys.com


L605

L -605 (Haynes ® 25 alloy)


L-605 is a solid solution strengthened cobalt-chromium-tungsten nickel alloy which combines excellent high temperature strength and oxidation resistance to 2000°F with good resistance to sulfidation, wear and galling. L-605 has good forming characteristics and is capable of being forged, hot worked or cold worked, althoug it does work-harden very rapidly so frequent intermediate annealing treatments are recommend for complex forming operations.  L-605 can also be readily welded by most conventional welding methods using similar composition welding wire (AMS 5796) or coated electrodes (AMS 5797). 

Nominal Composition %
Co 51.0
Ni 10.0
Fe 3.0 max
Cr 20.0
Mo 1.0 max
W 15.0
Mn 1.5
Si 0.4 max
C 0.1

Mechanical Properties
L-605 extruded bar @ Room Temperature
Tensile Strength 125ksi
Yield Strength 45ksi
Elongation 30%
Hardness 227 HB max
   

Specifications
UNS R30605
AMS5759
ASTM F90